Phase diagram and crystallography of the system Na2CrO4-K2CrO4
Goldberg, A.; Eysel, W.; Hahn, Th.
Neues Jahrbuch für Mineralogie - Monatshefte Jg. 1973 Heft 6 (1973), p. 241 - 252
18 references
published: Oct 29, 1973
DOI: 10.1127/njmm/1973/1973/241
ArtNo. ESP156197306000, Price: 19.00 €
Abstract
The system Na2CrO4-K2CrO4 was investigated by X-ray and thermal methods. The high-temperature modifications of Na2CrO4 and K2CrO4 reveal complete solubility. They are not isostructural with glaserite but correspond to high-K2SO4 and alpha-Ca2SiO4 with probable space group P63mc. The low-temperature forms low-Na2CrO4 (Ccmm), chrome-glaserite (P3m1) and low-K2CrO4 (Pcmm) form limited solid solutions. Chrome-glaserite is a solid solution and not a compound. In addition to the trigonal chrome-glaserite, monoclinic derivatives are described. The phase diagram, crystal chemistry and transformation enthalpies of the system Na2CrO4-K2CrO4 have a close bearing on the system Na2SO4-K2SO4.
Kurzfassung
Das System Na2CrO4-K2CrO4 wurde röntgenographisch und mit thermischen Methoden untersucht. Die Hochtemperaturformen von Na2CrO4 und K2CrO4 sind unbegrenzt mischbar. Sie kristallisieren nicht im Glaserittyp, sondern entsprechen Hoch-K2SO4 und alpha-Ca2SiO4 mit der wahrscheinlichen Raumgruppe P63mc. Die Tieftemperaturformen Tief-Na2CrO4 (Ccmm), Chromglaserit (P3m1) und Tief-K2CrO4 (Pcmm) zeigen begrenzte Mischbarkeit. Chromglaserit ist ein Mischkristall und keine Verbindung. Neben der trigonalen Form wurden monoklin deformierte Varianten gefunden. Phasendiagramm, Kristallchemie und Umwandlungswärmen des Systems Na2CrO4-K2CrO4 zeigen sehr enge Beziehungen zum System Na2SO4-K2SO4.
Keywords
Phase equilibria • sodium chromate • potassium chromate • X-ray diffraction • DTA