Contribution
The polymorphs of Cu8GeS6 - a preliminary study
Wang, Naiding; Viaene, Willy
Neues Jahrbuch für Mineralogie - Monatshefte Jg. 1974 Heft 10 (1974), p. 442 - 446
3 références bibliographiques
publié: Oct 9, 1974
DOI: 10.1127/njmm/1974/1974/442
ArtNo. ESP156197410002, Prix: 19.00 €
Abstract
The compound Cu8GeS6 crystallizes in two polymorphic forms. The high temperature form is stable above 57° C and not quenchable. The powder pattern can be indexed on a tetragonal unit cell of dimensions a0 = 7.03 Å and c0 = 9.92 Å. Powder pattern of the quenchable, low temperature form can be indexed on a related rhombohedral cell of arh = 9.89 Å and α = 89.7° Å. However, crystals of Cu8GeS6 grown at 850° C show a single crystal pattern with cubic symmetry. The rhombohedral symmetry is thought to be generated by a very slight, on the photographs not observable distortion of the cubic pattern in the direction of the 3-fold axis.
Kurzfassung
Die Verbindung Cu8GeS6 kristallisiert in zwei polymorphen Formen. Die Hochtemperaturform ist oberhalb 57° C stabil und nicht abschreckbar. Die Indizierung des Pulverdiagrammes ließ auf eine tetragonale Elementarzelle mit a0 = 7.03 Å und c0 = 9.92 Å schließen. Die Pulverdaten der abschreckbaren Tieftemperaturform ergaben eine rhomboedrische Zelle mit arh= 9.89 Å und α = 89.7°. Einkristallaufnahmen der bei 850° C gezüchteten Kristalle von Cu8GeS6 zeigten dagegen kubische Symmetrie. Es ist anzunehmen, daß die rhomboedrische Symmetrie durch eine geringe, auf den Einkristallaufnahmen jedoch nicht zu beobachtende Verzerrung der kubischen Zelle in Richtung der 3-zähligen Achse entstanden ist.
Mots-clefs
Cu-Ge sulphide • polymorphism • X-ray diffraction • DTA